Grain structure of Al – Si alloy at high-speed solidification. Taylor factor

Authors

  • Olga V. Gusakova International Sakharov Environmental Institute, Belarusian State University, 23/1 Dawgabrodskaja Street, Minsk 220070, Belarus
  • Vasily G. Shepelevich Belarusian State University, 4 Niezaliezhnasci Avenue, Minsk 220030, Belarus

Keywords:

Al – Si alloy, high-speed solidification, microstructure, grain structure, deformation, Taylor factor

Abstract

The grain structure of the foil of АK12оch alloy (Al – 12.3 wt. % Si – 0.2 wt. % Fe) is studied. The foil was produced by ultrafast quenching method from the melt at a cooling rate of 105 K/s. It exhibits a layered microstructure, which is due to changes in the thermodynamic conditions at the solid – melt phase during solidification. The grain structure of the aluminium phase in the foil layers was examined using backscattered electron diffraction. It was found that the average grain size in the foil layers is 3.5 and 4.6 μm. It was determined that in the foil layer adjacent to the crystallizer surface, the grain size distribution is bimodal. An explanation for the formation of foil areas with large (over 10 μm) and small (under 5 μm) grains is provided. It was established that in the foil layer adjacent to the crystalliser surface, deformation of large grains occurs due to tensile stress caused by the movement of the upper layers of the melt. The rotation of the grain’s crystal lattice is described using the Taylor model. Numerical values of the Taylor factor are given.

Author Biographies

  • Olga V. Gusakova, International Sakharov Environmental Institute, Belarusian State University, 23/1 Dawgabrodskaja Street, Minsk 220070, Belarus

    PhD (physics and mathematics), docent; associate professor at the department of nuclear and medical technologies, faculty of environmental monitoring

  • Vasily G. Shepelevich, Belarusian State University, 4 Niezaliezhnasci Avenue, Minsk 220030, Belarus

    doctor of science (physics and mathematics), full professor; professor at the department of solid state physics and nanotechnologies, faculty of physics

References

  1. Grosselle F, Timelli G, Bonollo F. Doe applied to microstructural and mechanical properties of Al – Si – Cu – Mg casting alloys for automotive applications. Materials Science and Engineering: A, Structural Materials Properties Microstructure and Processing. 2010;527(15):3536–3545. DOI: 10.1016/j.msea.2010.02.029.
  2. Godbole K, Bhushan B, Narayana Murty SVS, Mondal K. Al – Si controlled expansion alloys for electronic packaging applications. Progress in Materials Science. 2024;144:101268. DOI: 10.1016/j.pmatsci.2024.101268.
  3. Sathiyaseelan G, Bhagyanathan C, Srinath P, Gottmyers Melwyn J. Enhancing the strength and structure of Al – Si alloys for biomedical applications through the addition of Sr and Zr grain refiners on secondary AlSi7Mg aluminum alloys. Chemical Physics Impact. 2024;8:100557. DOI: 10.1016/j.chphi.2024.100557.
  4. Попова МВ, Прудников АН, Долгова СВ, Малюх МА. Перспективные алюминиевые сплавы для авиационной и космической техники. Вестник Сибирского государственного индустриального университета. 2017;3:18–23. EDN: ZHRDAH.
  5. Xu Y, Deng Y, Casari D, Mathiesen RH, Liu X, Li Y. Growth kinetics of primary Si particles in hypereutectic Al – Si alloys under the influence of P inoculation: experiments and modelling. Journal of Alloys and Compounds. 2021;854:155323. DOI: 10.1016/j.jallcom.2020.155323.
  6. Liang SS, Wen SP, Xu J, Wu XL, Gao KY, Huang H, et al. The influence of Sc – Si clusters on aging hardening behavior of dilute Al – Sc – (Zr) – (Si) alloy. Journal of Alloys and Compounds. 2020;842:155826. DOI: 10.1016/j.jallcom.2020.155826.
  7. Pracha O, Trudonoshyn O, Randelzhofer P, Körner С, Durst K. Multi-alloying effect of Sc, Zr, Cr on the Al – Mg – Si – Mn high-pressure die casting alloys. Materials Characterization. 2020;168:110537. DOI: 10.1016/j.matchar.2020.110537.
  8. Yang Y, Geng K, Li Sh, Bermingham M. Highly ductile hypereutectic Al – Si alloys fabricated by selective laser melting. Journal of Materials Science & Technology. 2022;110:84–95. DOI: 10.1016/j.jmst.2021.07.050.
  9. Zagulyaev D, Konovalov S, Gromov V, Glezer A, Ivanov Y, Sundeev R. Structure and properties changes of Al – Si alloy treated by pulsed electron beam. Materials Letters. 2018;229:377–380. DOI: 10.1016/j.matlet.2018.07.064.
  10. Cherenda NN, Tolkachov SA, Astashynski VM, Kuzmitski AM. Modification of composition, structure and mechanical properties of the surface layer of (Ti, Cu)N/Al – 12 at. % Si alloy system treated by compression plasma flows. Journal of the Belarusian State University. Physics. 2023;1:25–33.
  11. Li Y, Jiang T, Wei B, Xu B, Xu G, Wang Z. Microcharacterization and mechanical performance of an Al – 50Si alloy prepared using the sub-rapid solidification technique. Materials Letters. 2020;263:127287. DOI: 10.1016/j.matlet.2019.127287.
  12. Gusakova O, Shepelevich V, Alexandrov DV, Starodumov IO. Formation of the microstructure of rapidly solidified hypoeutectic Al – Si alloy. European Physical Journal Special Topics. 2020;229:417–425. DOI: 10.1140/epjst/e2019-900136-9.
  13. Гусакова ОВ, Шепелевич ВГ. Микроструктура и микротвердость сплава Al – Si, легированного Mg, Mn, Fe, Ni, Cu, при высокоскоростном затвердевании. Журнал Белорусского государственного университета. Физика. 2024;1:65–74. EDN: RSTXUW.
  14. Шварц А, Кумар М, Адамс Б, Филд Д, редакторы. Метод дифракции отраженных электронов в материаловедении. Москва: Техносфера; 2014. 544 с.
  15. Гусакова ОВ, Шепелевич ВГ, Александров ДВ, Стародумов ИО. Особенности формирования структуры сплавов Al – 12,2Si – 0,2Fe при сверхбыстрой закалке из расплава. Расплавы. 2020;2:138–148. DOI: 10.31857/S0235010620020048.
  16. Wei PS, Yeh FB. Heat transfer coefficient in rapid solidification of a liquid layer on a substrate. Journal of Heat Transfer. 2000;122(4):792–800. DOI: 10.1115/1.1318208.
  17. Wang W, Qiu HH. Interfacial thermal conductance in rapid contact solidification process. International Journal of Heat and Mass Transfer. 2002;45:2043–2053. DOI: 10.1016/S0017-9310(01)00307-6.
  18. Марширов ВВ, Марширова ЛЕ. Численное моделирование затвердевания сплавов при интенсивном сопряженном теплообмене. Сибирский журнал индустриальной математики. 2013;16(4):111–120. EDN: RHWMXN.
  19. Калиниченко AC, Кривошеев ЮК. Определение глубины переохлаждения расплава и характера структурообразования при закалке из жидкого состояния. Литье и металлургия. 2001;3:60–65.
  20. Дударев ЕФ. Микропластическая деформация и предел текучести поликристаллов. Томск: Издательство Томского государственного университета; 1988. 254 с.
  21. Taylor GI. Plastic strain in metals. Journal of the Institute of Metals. 1938;62:307–324.
  22. Лычагин ДВ. Фрагментация пластической деформации в металлических материалах с ГЦК-решеткой. Физическая мезомеханика. 2006;9(3):103–113.
  23. Balusu K, Kelton R, Meletis EI, Huang H. Investigating the relationship between grain orientation and surface height changes in nickel polycrystals under tensile plastic deformation. Mechanics of Materials. 2019;134:165–175. DOI: 10.1016/j.mechmat.2019.04.011.

Downloads

Published

2026-01-14

How to Cite

(1)
Gusakova, O. V.; Shepelevich, V. G. Grain Structure of Al – Si Alloy at High-Speed Solidification. Taylor Factor. Журнал Белорусского государственного университета. Физика 2026, No. 3, 24-32. https://doi.org/10.33581/2520-2243-2025-3-%p.